Inorganic zinc rich primer

Inorganic zinc rich primer applies to heavy anticorrosive primer in bottom material for thick plate steel, can be used alone, can be coated, high temperature resistant. Inorganic zinc rich primer can be used in anticorrosive oil tank, oil t



[ Product description]              

Inorganic zinc rich primer applies to heavy anticorrosive primer in bottom material for thick plate steel, can be used alone, can be coated, high temperature resistant. Inorganic zinc rich primer can be used in anticorrosive oil tank, oil tank, cargo, marine steel structure, high transmission tower harsh environments and large steel roof, chimney, offshore platform, chemical equipment such as rust. Inorganic zinc rich primer for waterborne inorganic zinc rich primer and alcohol soluble inorganic zinc rich primer two.

[ Product ].             

Two-component coating inorganic zinc rich primer by superfine zinc powder, modified resin made from zinc paste and ethyl silicate solution composition. Divided into waterborne inorganic zinc rich primer and alcohol soluble inorganic zinc rich primer two types.

[ The characteristics of the product]              

Li Inorganic zinc rich primer Has the properties of zinc rich paint salt fog, self repair after damage

In the surface of the coating can be matched with various types of anti-corrosion coating, can meet the needs of all kinds of long anticorrosion engineering

- excellent resistance to organic solvents, the electrochemical coating has excellent anticorrosion performance

In the continuous high temperature of 400-500 DEG C

In the low resistivity, antistatic, anti radiation, ultraviolet resistance, salt fog resistance, aging resistance, with long-lasting antiseptic effect

[ Basic data]

 

Impact strength (kg, CM)

Fifty

Gloss

No, light grey

Adhesion

Class A

Flexibility (mm)

One

Film hardness

1H

Drying time

Table dry = 1H, hard work (25 C) = 24h

Salt fog test

2500 hours (100 micron dry film surface is in good condition)

Aging test

1500 hours of intact surface

Heat resistance test

1500 hours of intact surface

High temperature, low temperature

-40 -500 OC


[
 Inorganic zinc rich primer Construction reference]              
  1. In the construction, should check the coating thickness, the thickness was found not up to the requirements, to timely repair paint, paint dry before or at the next time before spraying, coating should be protected, to prevent contamination or damage.
  2. After spraying the coating surface should be no trace, no leakage and blowout phenomenon, the film thickness should be uniform, consistent color. There shall be no rough, sagging, cracks, bubbles, peeling and other defects,
  3. In the corner, cut, weld and other components, should be the first to use manual brush inorganic zinc rich primer spraying, to ensure that the parts of the film thickness, while avoiding the paint in the recess is too thick when film cracking.
  4. Inorganic zinc rich primer can be used independently, can not finish, long-term corrosion, such as coating paint, paint must be fully cured, then coated with paint, the general interval is 24-48h.
  5.  

[ Security matters]           
  

- avoid skin and eye contact with inorganic zinc rich primer

If paint comes into contact with the skin, with warm water and appropriate cleaning agent, if paint comes into contact with the eyes, flush with plenty of water and seek immediate medical attention

To ensure good ventilation

The paint products contain flammable substances, please stay away from the spark of the prohibition of smoking in the neighborhood

The fire, the use of carbon dioxide gas, foam, and powder fire extinguisher

- before operation, please refer to the "safety precautions"